Chemical Composition of Aluminium alloy 6082
Table 1. Chemical composition for aluminium alloy 6082
| Element | % Present |
|---|---|
| Si | 0.7-1.3 |
| Fe | 0.0-0.5 |
| Cu | 0.0-0.1 |
| Mn | 0.4-1.0 |
| Mg | 0.6-1.2 |
| Zn | 0.0-0.2 |
| Ti | 0.0-0.1 |
| Cr | 0.0-0.25 |
| Al | Balance |
Properties of Aluminium alloy 6082
Mechanical Properties of Aluminium alloy 6082
Table 2 (a). Mechanical properties for aluminium alloy 6082 Soft O
|
BS EN 485-2:2008 Sheet 0.4mm to 6.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 85 Max MPa |
| Tensile Strength | 150 Max MPa |
| Hardness Brinell | 40 HB |
*Properties above are for material in the Soft O condition
Table 2 (b). Mechanical properties for aluminium alloy 6082 T4
|
BS EN 755-2:2008 Extruded Rod,Bar,Tube & Profiles Up to 200mm Dia.or A/F, Up to 25mm WT tube & Prof |
|
|---|---|
| Property | Value |
| Proof Stress | 110 Min MPa |
| Tensile Strength | 205 Min MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 70 HB |
| Elongation A | 14 Min % |
*Properties above are for material in the T4 condition
Table 2 (c). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Rod & Bar Up to 20mm Dia. & A/F |
|
|---|---|
| Property | Value |
| Proof Stress | 250 Min MPa |
| Tensile Strength | 295 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 8 Min % |
*Properties above are for material in the T6 condition
Table 2 (d). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Rod & Bar 20mm to 150mm Dia. & A/F |
|
|---|---|
| Property | Value |
| Proof Stress | 260 Min MPa |
| Tensile Strength | 310 Min MPa |
| Hardness Brinell | 95 HB |
| Elongation A | 8 Min % |
*Properties above are for material in the T6 condition
Table 2 (e). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Bar 150mm to 200mm Dia. & A/F |
|
|---|---|
| Property | Value |
| Proof Stress | 240 Min MPa |
| Tensile Strength | 280 Min MPa |
| Hardness Brinell | 95 HB |
| Elongation A | 6 Min % |
*Properties above are for material in the T6 condition
Table 2 (f). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Bar 200mm to 250mm Dia. & A/F |
|
|---|---|
| Property | Value |
| Proof Stress | 200 Min MPa |
| Tensile Strength | 270 Min MPa |
| Hardness Brinell | 95 HB |
| Elongation A | 6 Min % |
*Properties above are for material in the T6 condition
Table 2 (g). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Tube Up to 5mm Wall Thickness |
|
|---|---|
| Property | Value |
| Proof Stress | 250 Min MPa |
| Tensile Strength | 290 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 8 Min % |
*Properties above are for material in the T6 condition
Table 2 (h). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Tube 5mm to 25mm Wall Thickness |
|
|---|---|
| Property | Value |
| Proof Stress | 260 Min MPa |
| Tensile Strength | 310 Min MPa |
| Elongation A50 mm | 8 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 10 Min % |
*Properties above are for material in the T6 condition
Table 2 (i). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Open & Hollow Profile Up To 5mm Wall Thickness |
|
|---|---|
| Property | Value |
| Proof Stress | 250 Min MPa |
| Tensile Strength | 290 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 8 Min % |
*Properties above are for material in the T6 condition
Table 2 (j). Mechanical properties for aluminium alloy 6082 T6
|
BS EN 755-2:2008 Open & Hollow Profile 5mm to 25mm Wall Thickness |
|
|---|---|
| Property | Value |
| Proof Stress | 260 Min MPa |
| Tensile Strength | 310 Min MPa |
| Elongation A50 mm | 8 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 10 Min % |
*Properties above are for material in the T6 condition
Table 2 (k). Mechanical properties for aluminium alloy 6082 T6 / T651
|
BS EN 485-2:2008 Plate 6.00m to 12.5mm |
|
|---|---|
| Property | Value |
| Proof Stress | 255 Min MPa |
| Tensile Strength | 300 Min MPa |
| Elongation A50 mm | 9 Min % |
| Hardness Brinell | 91 HB |
*Properties above are for material in the T6 and T651 condition
Table 2 (l). Mechanical properties for aluminium alloy 6082 T6 / T651
|
BS EN 485-2:2008 Plate 12.5mm to 100.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 240 Min MPa |
| Tensile Strength | 295 Min MPa |
| Hardness Brinell | 89 HB |
*Properties above are for material in the T6 and T651 condition
Table 2 (m). Mechanical properties for aluminium alloy 6082 T6 / T651
|
BS EN 485-2:2008 Plate 100.00mm to 150.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 240 Min MPa |
| Tensile Strength | 275 Min MPa |
| Hardness Brinell | 84 HB |
| Elongation A | 6 Min % |
*Properties above are for material in the T6 and T651 condition
Table 2 (n). Mechanical properties for aluminium alloy T6 / T651 (rolled products)
|
BS EN 485-2:2008 Sheet 0.4mm to 6.00mm |
|
|---|---|
| Property | Value |
| Proof Stress | 260 Min MPa |
| Tensile Strength | 310 Min MPa |
| Hardness Brinell | 94 HB |
*Properties above are for material in the T6 condition and, for rolled products, the T651 condition
Table 3. Physical properties for aluminium alloy 6082
| Property | Value |
|---|---|
| Density | 2700 kg/m3 |
| Melting Point | 555°C |
| Modulus of Elasticity | 70 GPa |
| Electrical Resistivity | 0.38 x 10-6 Ω.m |
| Thermal Conductivity | 180 W/m.K |
| Thermal Expansion | 24 x 10-6/K |
Applications of Aluminium alloy 6082
Aluminium alloy 6082 is used in:
Supplied Forms
Aluminium alloy 6082 is available from Aalco in the following forms with a T6 temper:
If you need product information or price, please fill in your contact information in the form, we will usually contact you within 12 hours. You could also email me info@lyapm.com to get prompt reply.
NO.501 Dongshe Road, Dongjing Town, Songjiang District, Shanghai,China,201600
. 
Mobile/Whatsapp/Zalo/Lines/Skype
General Inquiry
company profile download