AISI 1572 Carbon steel Chemical composition and Mechanical properties
| Element | Weight % |
| C | 0.65-0.76 |
| Mn | 1.00-1.30 |
| P | 0.04 (max) |
| S | 0.05 (max) |
We can produce the AISI 1572 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
AISI 1572 Carbon steel
Steel grade type Carbon steel: Standard AISI Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings. Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.Range of work Round bar steel: 1mm to 2000mm
Square-shape steel: 10mm to 1000mm
steel Plate/sheet:0.08mm to 800mm
Width: 10mm to 1500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.
Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing AISI 1572 Carbon steel Chemical composition and Mechanical properties
Element Weight % C 0.65-0.76 Mn 1.00-1.30 P 0.04 (max) S 0.05 (max) Mechanical Properties
Thermal Properties
Properties Conditions T (°C) Treatment Density (×1000 kg/m3) 7.7-8.03 25 Poisson's Ratio 0.27-0.30 25 Elastic Modulus (GPa) 190-210 25 Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C Yield Strength (Mpa) 1034 Elongation (%) 15 Reduction in Area (%) 53 Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C
Properties Conditions T (°C) Treatment Thermal Conductivity (W/m-K) 42.7 100 Specific Heat (J/kg-K) 477 50-100 Physical Properties
Quantity Value Unit Thermal expansion 16 - 17 e-6/K Thermal conductivity 16 - 16 W/m.K Specific heat 500 - 500 J/kg.K Melting temperature 1370 - 1400 °C Service temperature 0 - 500 °C Density 8000 - 8000 kg/m3 Resistivity 0.7 - 0.7 Ohm.mm2/m
Machining performance
Download AISI 1572 the mechanical properties of the report, the report provides detailed performance analysis and application.
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
If you need product information or price, please fill in your contact information in the form below, we will usually contact you within 12 hours. You could also email me info@lyapm.com to get prompt reply.
NO.501 Dongshe Road, Dongjing Town, Songjiang District, Shanghai,China,201600
. 
Mobile/Whatsapp/Zalo/Lines/Skype
General Inquiry
company profile download